Powder Coating Epoxy High Tamperature Fast Curing Agent Tp41
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Anhui
-
Validity to:
Long-term effective
-
Last update:
2017-08-12 01:20
-
Browse the number:
260
+
Shandong Jufu Chemical Technology Co., Ltd.
- Contactaixin:
Miss Jane(Mr.)
- Email: telephone: phone:
-
Arrea:
Anhui
Address:No. 88 of Huizhan West Road, High-Tech Zone, Jinan, Shandong, China 250101
- Website:
+
TP41-Epoxy Hardener For Anti-corrosive Powder Coating
Describe:
TP41, the curing agent is a phenolic excess type curing agent . Due to the high activity of the hydroxyl, can rapidly react with the epoxy groups, which can achieve high-temperature fast curing. Suitable for the manufacture of heavy-duty powder coating.
Technical indicators:
Recommended ratio:
Epoxy resin (E12)which is equivalnet to YD-014 / HARDENER TP41 = 100/20
Reference formulation:
Curing condition:
160ºC at 15min or 200ºC at 3 min
Other describe:
Add a small amount of a curing accelerator, such as 2 - methylimidazole ,2 - phenylimidazole morpholine, etc. can be adjusted to the requirements of the curing temperature and curing time.
Baking temperature:
Add 0.1% curing accelerator can be realized 200C, three minute cure or 160c at 10 minute cure.
Packaging, storage and transportation:
Kraft paper bag, net weight 25kg.Storage in a cool, dry, well-ventilated place to prevent the sun and rain, should be cut off from the high-temperature and fire.
Describe:
TP41, the curing agent is a phenolic excess type curing agent . Due to the high activity of the hydroxyl, can rapidly react with the epoxy groups, which can achieve high-temperature fast curing. Suitable for the manufacture of heavy-duty powder coating.
Technical indicators:
Appearance | Crystalline solid |
Softening point | 78-90ºC |
Epoxy equivalent weight | 240-260 |
Viscidity 25ºC m Pas | 100-140(150ºC) |
Recommended ratio:
Epoxy resin (E12)which is equivalnet to YD-014 / HARDENER TP41 = 100/20
Reference formulation:
EPOXY RESIN | 200 |
FLOWING AGENT TP88 | 4 |
TI02 | 80 |
BASO4 | 80 |
HARDENER TP41 | 40 |
2-Isopropylimdazole | 1 |
Curing condition:
160ºC at 15min or 200ºC at 3 min
Other describe:
Add a small amount of a curing accelerator, such as 2 - methylimidazole ,2 - phenylimidazole morpholine, etc. can be adjusted to the requirements of the curing temperature and curing time.
Baking temperature:
Add 0.1% curing accelerator can be realized 200C, three minute cure or 160c at 10 minute cure.
Packaging, storage and transportation:
Kraft paper bag, net weight 25kg.Storage in a cool, dry, well-ventilated place to prevent the sun and rain, should be cut off from the high-temperature and fire.